Hydrothermal Solution of Heavy Metals from MSWI Fly Ashes
The solid residues produced during municipal solid waste incineration (MSWI) may be grouped into bottom ashes and fly ashes, which contain appreciable amounts of Fe and non-iron (NE) metals as well. Pure metals like Fe, Al or Cu can be separated from the bottom ashes by physical methods but there are no attempts to extract NE metals which are incorporated in oxide, chloride
or silicate mineral phases like Zn and Pb. In MSWI bottom ashes the Zn- and Pb contents vary from 2000 ppm up to 7000 ppm and 1000 ppm up to 3500 ppm, respectively.
The fly ashes were usually collect by filters like electrostatic precipitator (ESP). In ESP residues the Zn- and the Pb contents are much higher covering a range from 5000 ppm up to 100000 ppm for Zn and from2500 ppm up to 25000 ppm for Pb, respectively. Due to the high concentration of heavy metals as well as trace amounts of organic pollutants (dioxins, furans) the ESP residues are classified as hazardous material. In the last years a paradigm change took place. Now hazardous material becomes a resource for the heavy metals if the organic pollutants can be destroyed. A promising technique is the hydrothermal solution, transport and precipitation leading to separation and enrichmentof heavy metal compounds. In addition dioxins and furans were destroyed in the presence of an oxy-hydrous vapor phase. The yellowish material exists of spherical glass droplets of ca. 100 μm diameter, condensed alkali-chlorides and black carbon particles. Some of the glassdroplets are devitrified forming gehlenite, clinopyroxene and spinel. The grain size Distribution shows a polymodal shape. With d10 at 1 μm and d50 at 128 μm. The Zn- and Pb-content of the investigated ESP residues are 42071 ppm for Zn and 26380 ppm for Pb as determined by X-RayFluorescence Analysis (XRF). The Zn- and Pb-bearing mineral phases were characterized by XRay Powder Diffraction (XRPD) and Electron Microprobe Analysis (EMPA).
| Copyright: | © Lehrstuhl für Abfallverwertungstechnik und Abfallwirtschaft der Montanuniversität Leoben | |
| Quelle: | Depotech 2014 (November 2014) | |
| Seiten: | 1 | |
| Preis inkl. MwSt.: | € 0,00 | |
| Autor: | Amanda Günther  | |
| Artikel weiterleiten | Artikel kostenfrei anzeigen | Artikel kommentieren |
Diese Fachartikel könnten Sie auch interessieren:
Development of local municipal solid waste management in the Western Transdanubia region of Hungary
© Lehrstuhl für Abfallverwertungstechnik und Abfallwirtschaft der Montanuniversität Leoben (11/2020)
Hungarian municipal solid wastes (MSW) management has developed tremendously over the past 15 years. More than 3,000 landfills and dumps had been closed, just to mention one improvement. However, still, lots of work is necessary to accomplish the EU’s ambitious aim of decreasing landfilling and increasing recycling and composting.
bifa-Text Nr. 67: Umweltrisiken der Nanotechnologie: Sicherung der Kreislaufwirtschaft mit biologischen Testverfahren
© bifa Umweltinstitut GmbH (3/2016)
Es wurde vom bifa Umweltinstitut die Wirkung ausgewählter Nanomaterialien auf aerobe und anaerobe Abbauvorgänge in verschiedenen biologischen Testverfahren untersucht.
Steel Slag Asphalt: Preventing the Waste of a High Quality Resource
© Lehrstuhl für Abfallverwertungstechnik und Abfallwirtschaft der Montanuniversität Leoben (11/2014)
Steel slag is the inevitable by-product of the production of steel, from both the conversion of iron to steel and the recycling of steel scrap. Historically, this material has been sent to a landfi ll as waste, but over the last 100 years or so, a variety of uses have been found for what has proven to be a high quality, valuable resource. With this in mind, the steel industry within Europe now consider iron and steel slag to be products and not waste and as such have registered the materials under Reach (Registration, Evaluation Authorization and Restriction of Chemicals). Steel slag is formed by the addition of lime to the molten metal in order to remove impurities and to control the quality of the steel. The resultant slag is a complex mineral formed from oxides of calcium, aluminium, silicon and magnesium along with various other trace elements. Once cooled, the slag forms a crystalline rock that can be used as a replacement for natural aggregate in a variety of construction products, including asphalt. This paper specifi cally focuses on the use of steel slag as aggregate for asphalt mixtures in road construction and addresses the processing and quality control of the slag, along with its properties and the benefit of these properties for Asphalt materials.
Abtrennung und Verwertung von Glas aus Wirbelschicht-Bettasche
© Lehrstuhl für Abfallverwertungstechnik und Abfallwirtschaft der Montanuniversität Leoben (11/2014)
Bettasche aus Wirbelschichtöfen kann zu drei Viertel verwertet werden. Für ein hochwertiges Recycling stehen Metalle – Eisen/Stahl, Aluminium, sonst. Buntmetalle, Edelstähle und Glas zur Verfügung. Glasteile aus Bettasche können zur Herstellung eines hochwertigen Isolier- und Baumaterials eingesetzt werden – zur Herstellung von Schaumglas.
Interessante Aufschlüsse - Die UMTEC-Methode zur Bestimmung der Metallgehalte in MVA-Schlacken liefert exakte Ergebnisse
© Rhombos Verlag (8/2014)
Abfälle wurden bis vor wenigen Jahren überwiegend aus der Schadstoffperspektive betrachtet und als umweltschädlich angesehen. Mittlerweile hat sich die Erkenntnis durchgesetzt, dass Abfälle auch als Sekundärrohstoffe betrachtet werden können (Ressourcenperspektive). Die Separatsammlung stellt eine Möglichkeit dar, Wertstoffe aus Abfällen zu gewinnen. In diesem Fall führt der Konsument stark wertstoffhaltige Abfallfraktionen einer direkten Verwertung zu (etwa Altmetalle, Elektronikschrott oder Batterien). Dennoch verbleiben im Haus- und Gewerbemüll noch erhebliche Mengen an Wertstoffen, insbesondere Metalle.